Aluminum Silicate Refractory Fiber Felt for furnace liner

FOB Reference Price:Get Latest Price
$5.00 - $10.00 / Rolls | 1 Roll/Rolls (Min. Order)
Report Suspicious Activity
Overview
Quick Details
Grade:
HA (High Aluminum)
Application:
Liners Of Industrial Furnace
Thickness:
25
Width:
600
Length:
7200
Chemical Composition:
Al2O3
Working Temperature:
1400
Fiber Diameter:
2.8
Shrinkage (1800 ℉, 3h):
18
Thermal Conductivity:
3
Density (kg/m³ ):
128
Model Number:
1260
Brand Name:
Sunrise
Place of Origin:
Henan, China (Mainland)
Shape:
blanket
Material:
Al2O3
Supply Ability
Supply Ability:
2000 Ton/Tons per Month
Packaging & Delivery
Packaging Details
carton, then wooden pallet and then polyethylene film is placed over it, finally the package is tied up with strips
Port
Shanghai/Qingdao/Tianjin

Specifications

1.Excellent thermal stability
2.Excellent chemistry quality
3.Resistance to burning
4.Low thermal conductivity

High quality Aluminum Silicate Refractory Fiber Felt

 

SUNRISE CERAMIC FIBRE BLANKET is made of special ceramic long-fiber that is produced by the melting of very pure raw materials in double surface needing process without binders and with good stability in a large range of temperature. The process of double surface needling increases interweaving and tensile strength

 

Characteristic

Contain Zirconia

 Non-combustible

Can withstand temperature up to 2600oF

Low density and low thermal conductivity

Shorter heat up and cool down time

Resilience and resistance to thermal shock

Flexible and easy to cut or install  

Consist of acoustic properties

Contain no organic binder

 

 Application:

Direct exposure to heat as furnace hot face lining

Expansion joint seal

Fire protection

 

Classification temperature

1425oC (2600o F)

Melting point

1700oC (3100o F)

Fiber diameter

2.8 micro meter

Fiber length

100 mm average. ~250 mm max.

Tensile strength

3.6 kg / 25 x 25 mm of 128 kg / m3 on 25 mm thickness

 

 

Specification

Average

Bulk density

 

kg / m3

150~195

115~150

 85~115

160

128

 96

Liner shrinkage

1200oC x 8hrs

%

<  3

1.5

Shot content

 >212micro meter

%

<  25

18

Chemical composition %

Al2O3

>  32

35.0

ZrO2

>  13

15.0

SiO2

<  55

49.7